甲壳素纳米纤维/聚乳酸复合材料的制备及性能
Preparation and Properties of Chitin Nanofibers/Polylactic Acid Composite
Author:
Jingjing Li1, Jingfeng Zhao1, Jingrong Sun1, Dagang Li2Jingjing Li1, Jingfeng Zhao1, Jingrong Sun1, Dagang Li2
1. College of Forestry, Northwest A&F University, Yangling 712100, China; 2. College of Materials Science and Engineering，Nanjing Forestry University，Nanjing 210037, China
在期刊界中查找
在百度中查找
在本站中查找
摘要:
利用甲壳素纳米纤维（CHNFs）对聚乳酸（PLA）进行增强改性，分别采用湿混法和聚乙二醇（PEG）分散剂法制备了挤出成型的CHNFs/PLA复合材料，并对复合材料的力学性能、热性能及微观形貌进行表征。结果表明，制备的α-甲壳素纳米纤维直径小于100 nm，长度为几百微米，具有三维网状结构；湿混法和PEG分散剂法对制备的CHNFs/PLA复合材料都有较好的增强作用，当CHNFs的添加量高于30%时，湿混法制备的复合材料的力学性能明显优于PEG分散剂法制备的复合材料；对复合材料的扫描电镜图分析表明，湿混法制备的复合材料中有大量的网状细丝均匀致密地分散在PLA的断面，达到了对CHNFs预期的分散效果，而PEG分散剂法制备的复合材料中，CHNFs以短小纤维的聚集体形态分布于复合材料的断面，说明聚乙二醇对于CHNFs与PLA体系是良好的界面相容剂，但是该方法降低了CHNFs的长径比。因此湿混法是一种更有效的纤维预处理方式。
Abstract:
Chitin nanofibers (CHNFs) reinforced polylactic acid (PLA) composites were prepared by the wet blending method and the polyethylene glycol(PEG) dispersion agent method. The properties of mechanical, thermal and microscopic for CHNFs/PLA composites were investigated. The results demonstrate that the diameter of obtained α-chitin nanofibers is less than 100 nm and the length is about several hundreds of micrometer with three-dimensional network structure. An ideal reinforcing effect can be achieved for CHNFs/PLA samples prepared by these two methods. When the content of CHNFs is higher than 30%, the mechanical performance of the composite prepared by the wet blending method is better than that of the composite prepared by the PEG method. From the FE-SEM images, it is found that a large number of fibers are distributed on the fracture surface of PLA uniformly and compactly for the samples prepared by the wet blending method. For the samples prepared by the PEG method, some short fiber clusters are entangled with PLA matrix with no obvious phase separation between CHNFs and PLA. This observation reveals that PEG is a good interfacial compatibilizer for CHNFs and PLA. However, the reinforcing effect is weaken due to decrement of the CHNFs aspect ratio for the PEG method, and the wet blending method is an effective pretreatment method for nanofibers．
引用本文李晶晶, 赵泾峰, 孙景荣, 李大纲.甲壳素纳米纤维/聚乳酸复合材料的制备及性能[J].高分子材料科学与工程,2017,33(3):161-167.
复制
分享 文章指标 点击次数:961 下载次数: 0 HTML阅读次数: 0相关知识
膳食纤维和纤维素的区别
甲壳素减肥有没有副作用
彩韵纳米内墙漆健康环保的**材料
芫根复合维生素饮料的制作及其抗疲劳功能评价
9大类室内空气净化材料
一种家具用无甲醛胶黏剂及其制备方法技术
全用环保材料就没甲醛了？你家里可能还藏着这些“隐形杀手”
银纤维防辐射服
2024年纳米银抗菌灵项目可行性研究报告.docx
微塑料的人体富集及毒性机制研究进展
网址: 甲壳素纳米纤维/聚乳酸复合材料的制备及性能 https://m.trfsz.com/newsview364278.html